Polyester cotton

polyester cotton
Polyester processing

After the first stage of polymer production in the melt phase, the product stream divides into two different application areas which are mainly textile applications and packaging applications. In figure 2 the main applications of textile and packaging polyester are listed.

Table 2: Textile and packaging polyester application list
POLYESTER-BASED POLYMER (MELT or PELLET)
Textile Packaging
Staple fiber (PSF) Bottles for CSD, Water, Beer, Juice, Detergents
Filaments POY, DTY, FDY A-PET Film
Technical yarn and tire cord Thermoforming
Non-woven and spunbond BO-PET Biaxial oriented Film
Mono-filament Strapping

Abbreviations: PSF = Polyester Staple Fiber; POY = Partially Oriented Yarn; DTY = Draw Textured Yarn; FDY = Fully Drawn Yarn; CSD = Carbonated Soft Drink; A-PET = Amorphous Polyester Film; BO-PET = Biaxial Oriented Polyester Film;

A comparable small market segment (<< 1 Million t/a) of polyester is used to produce engineering plastics and masterbatch.

In order to produce the polyester melt with a high efficiency, high-output processing steps like staple fiber (50–300 t/d per spinning line) or POY /FDY (up to 600 t/d split into about 10 spinning machines) are meanwhile more and more horizontal, integrated, direct processes. This means the polymer melt is directly converted into the textile fibers or filaments without the common step of pelletizing. We are talking about full horizontal integration when polyester is produced at one site starting from crude oil or distillation products in the chain oil -> benzene -> PX -> PTA -> PET melt -> fiber / filament or bottle-grade resin. Such integrated processes are meanwhile established in more or less interrupted processes at one production site. Eastman Chemicals introduced at first the idea to close the chain from PX to PET resin with their so-called INTEGREX process. The capacity of such horizontal, integrated productions sites is >1000 t/d and can easily reach 2500 t/d.

Besides the above mentioned large processing units to produce staple fiber or yarns, there are ten thousands of small and very small processing plants, so that one can estimate that polyester is processed and recycled in more than 10 000 plants around the globe. This is without counting all the companies involved in the supply industry, beginning with engineering and processing machines and ending with special additives, stabilizers and colors. This is a gigantic industry complex and it is still growing by 4–8% per annum, depending on the world region. Useful information about the polyester industry can be found under [5] where a “Who is Producing What in the Polyester Industry” is gradually being developed.
Ring-opening polymerization

Aliphatic polyesters can be assembled from lactones under very mild conditions, catalyzed anionically, cationically or metallorganically.

Thermosetting resins are generally copolymers of unsaturated polyesters with styrene. Polyester saturation is governed through the use of maleic acid or fumaric acid. In vinyl esters, saturation (or lack thereof) is found in the alcohol group of the polyester. The double bond of unsaturated polyester reacts with styrene resulting in a 3-D cross-linked structure. This structure acts as a thermoset. The cross-linking is initiated through an exothermic reaction involving an organic peroxide, such as methyl ethyl ketone peroxide or benzoyl peroxide.